PC/ABS is a modified engineering plastic synthesized by mixing. Among them, PC is polycarbonate, ABS is acrylonitrile (A), butadiene (B) and styrene (S) copolymer. PC has strong impact resistance, high heat resistance, ABS has very good toughness, so this material is better than a single PC or ABS performance, the price is more expensive. Due to its high heat resistance, PC/ABS is often used in automotive interior parts, electronic equipment housing, computer housing and other products that require high temperature resistance.
| PC/ABS | LUPOY GN5001RFZ | NH-1015V | Cycoloy* Resin C6200 | JH960-HT08 | Unit | Testing Standard |
| Data sheet | Click to Download | Click to Download | Click to Download | Click to Download | ||
| Manufacturer | LG | Samsung | SABIC | KINGFA | ||
| Description | Halogen Free Flame Retardent, Heat Resistance | Resin Type： PC/ABS | Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs. | Halogen-free FR V-0, Excellent mechanical properties, High heat resistance, Improved Chemical resistance | ||
| Appearance | Natural color | Natural color | Natural color | Natural color | ||
| UL Yellow Card | / | / | / | / | ||
| Physical | Dry | Dry | Dry | Dry | Unit | Test Method |
| Specific Gravity | 1.19 | 1.17 | 1..18 | 1.19 | / | ASTM D792 |
| Melt Flow Index | 15 | 30 | 14.5 | 18 | g/10min | ASTM D1238 |
| Mold Shrinkage(MD) | 0.4~0.6 | 0.5~0.7 | 0.4~0.6 | 0.4~0.6 | % | ASTM D955 |
| Mechanical | Dry | Dry | Dry | Dry | Unit | Test Method |
| Flexural Modulus | 25000 | 24000 | 2680( MPa) | 2500( MPa) | kgf/cm² | ASTM D790 |
| Flexural Strength | 1100 | 890 | 103( MPa) | 90( MPa) | kgf/cm² | ASTM D790 |
| Tensile Strength(Yield) | 600 | 650 | 66(MPa ) | 60( MPa) | kg/cm² | ASTM D638 |
| Tensile Elongation(Break) | 80 | / | 50 | 50 | % | ASTM D638 |
| Impact | Dry | Dry | Dry | Dry | Unit | Test Method |
| Notched lzod Impact Strength(23°C) | 55 | 55 | 534(J/m ) | 550(J/m ) | kg·cm/cm | ASTM D256 |
| Thermal | Dry | Dry | Dry | Dry | Unit | Test Method |
| Heat Deflection Temperature at 1.8 Mpa | 101 | 86 | 87 | 93 | °C | ASTM D648 |
| Relative Temp Index, Elec | 80 | 90 | 85 | / | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | 85 | 85 | / | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 85 | 90 | 85 | / | °C | UL 746B |
| Electrical | Dry | Dry | Dry | Dry | Unit | Test Method |
| Comparative Tracking Index | / | / | 2 | / | PLC Code | UL 746A |
| Flammability | Dry | Dry | Dry | Dry | Unit | Test Method |
| 1.5mm | V-0,5VB | V-0,5VB | V-0VB | V-0,5VB | class | UL94 |
| 2.0mm | V-0,5VB | 5VB | 5VB | / | class | UL94 |